@article { ISI:000236922600002,
	title = {Room temperature synthesis of mesoporous aggregates of anatase TiO2 nanoparticles},
	journal = {Materials Chemistry and Physics},
	volume = {97},
	number = {2-3},
	year = {2006},
	month = {JUN},
	pages = {207-212},
	publisher = {ELSEVIER SCIENCE SA},
	type = {Article},
	address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND},
	abstract = {<p>The controlled hydrolysis reaction of titanium tetrabutoxide in presence of acetic acid in isopropanol, i.e. in non-aqueous media was adopted in the present work for the synthesis of nanocrystalline titania followed by aging at ambient conditions for longer duration. The powder XRD shows that the as-dried precursor (without any aging) is non-crystalline in nature. However, room temperature aging for longer duration \&gt; 120 days not only helped to develop crystallinity in TiO2 nanoparticles but also led to the formation of their self-assembly towards mesoporous aggregates creating sponge like TiO2 nano-structure having high surface area similar to 250m (2) g(-1)and narrow pore size distribution of 4-5 nm. TEM observations revealed the generation of spherical TiO2 nanoparticles (4-5 nm) assembled to form stable spongy scaffold having porous network structure with pore size 5-6 nm. Also, presence of a pronounced hysteresis loop in BET isotherm is indicative of a 3D-intersection network of the pores of size 4-5 nm. Further heat-treatment to the aged precursor at 400 degrees C/2 h in air modify pore network structure due to sintering of TiO2 particles as is observed in TEM studies and lowering thereby the surface area to 125 m(2) g(-1) (c) 2005 Elsevier B.V. All rights reserved.</p>},
	keywords = {Microstructure, porous materials, sol-gel processing, titania},
	issn = {0254-0584},
	doi = {10.1016/j.matchemphys.2005.02.014},
	author = {Deshpande, S. B. and Potdar, H. S. and Khollam, Y. B. and Patil, K. R. and Pasricha, R. and Jacob, Nalini E.}
}
@article { ISI:000248795100038,
	title = {Titania nanoparticles synthesis in mesoporous molecular sieve MCM-41},
	journal = {Journal of Colloid and Interface Science},
	volume = {314},
	number = {1},
	year = {2007},
	month = {OCT},
	pages = {310-316},
	publisher = {ACADEMIC PRESS INC ELSEVIER SCIENCE},
	type = {Article},
	address = {525 B ST, STE 1900, SAN DIEGO, CA 92101-4495 USA},
	abstract = {<p>Nanocrystalline titanium oxide (TiO2) is one of the most useful oxide material, because of its widespread applications in photocatalysis, solar energy conversion, sensors and optoelectronics. The control of particle size and monodispersity of TiO2 nanoparticles is a challenging task. The use of MCM-41, an inorganic template of uniform pore size (2-10 nm), can overcome this difficulty and produce stable nanoparticles of uniform size and shape. Here, we demonstrate the synthesis of titania nanoparticles inside the pores of silica based MCM-41 forming a TiO2/Si-MCM composite. Composites are formed in the alcoholic medium by incipient wetness impregnation method. Titania particles of average 3 nm size are obtained. Effect of silica and titania precursors on the quality of nanoparticles has been investigated. The characterization of titania-MCM-41 composites has been carried out using a variety of techniques like UV-vis absorption spectroscopy, X-ray diffraction, FT-IR spectroscopy, X-ray photoelectron spectroscopy, transmission electron microscopy and photoluminescence spectroscopy. It has been found that the titania particles are co-ordinated with Si-MCM by Si-O-Ti covalent bond. (C) 2007 Elsevier Inc. All rights reserved.</p>},
	keywords = {incipient wetness impregnation, Mesoporous material, template, titania},
	issn = {0021-9797},
	doi = {10.1016/j.jcis.2007.05.069},
	author = {Lihitkar, N. B. and Abyaneh, Majid Kazemian and Samuel, V. and Pasricha, R. and Gosavi, S. W. and Kulkarni, S. K.}
}