@article { ISI:000239671800023, title = {Cobalt-containing hexagonal mesoporous molecular sieves (Co-HMS): Synthesis, characterization and catalytic activity in the oxidation reaction of ethylbenzene}, journal = {Journal of Molecular Catalysis A-Chemical}, volume = {255}, number = {1-2}, year = {2006}, month = {AUG}, pages = {123-130}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

Cobalt-containing hexagonal mesoporous materials (Co-HMS and Co/HMS) with different cobalt content were synthesized for the first time by direct hydrothermal and post-synthesis (grafting) method. The materials were characterized in detail by X-ray diffraction, BET surface area, N-2 sorption isotherms, SEM, TEM, UV-vis and XPS techniques. Powder X-ray diffraction pattern, N2 adsorption-desorption analysis and TEM analysis show the presence of hexagonal mesoporous structure, having Type W isotherms and reveals the typical wormhole-like morphology. Spectroscopic techniques like UV-vis and XPS reveal cobalt in +2 oxidation state and tetrahedrally coordinated. Liquid phase oxidation of ethylbenzene using TBHP (70 wt\%) as an oxidant shows that the catalysts are highly active, under solvent free conditions as well as under lower cobalt concentrations. Leaching studies performed by hot filtration experiments show that the cobalt catalysts prepared by hydrothermal methods are stable, while the grafted catalysts show the leaching of cobalt under the reaction conditions. (c) 2006 Elsevier B.V. All rights reserved.

}, keywords = {Co-HMS, ethylbenzene, HMS, hydrothermal, Oxidation}, issn = {1381-1169}, doi = {10.1016/j.molcata.2006.03.072}, author = {Bhoware, Shrikant S. and Shylesh, S. and Kamble, K. R. and Singh, A. P.} } @article { ISI:000270363600029, title = {Enhanced conversion efficiency in dye-sensitized solar cells based on hydrothermally synthesized TiO2-MWCNT nanocomposites}, journal = {ACS Applied Materials \& Interfaces}, volume = {1}, number = {9}, year = {2009}, month = {SEP}, pages = {2030-2035}, publisher = {AMER CHEMICAL SOC}, address = {1155 16TH ST, NW, WASHINGTON, DC 20036 USA}, abstract = {

A 50 \% enhancement in the conversion efficiency (4.9-7.37 \%) is realized in dye-sensitized solar cells Using hydrothermally synthesized TiO2-multiwalled carbon nanotube (MWCNT) nanocomposites as compared to hydrothermally synthesized TiO2 without MWCNT and Degussa P25. Several characterizations have been employed to reveal the nature of the modification imparted to the MWCNTs under hydrothermal processing conditions and the resulting TiO2-MWCNT conjugation through -COOH groups. Efficient charge transfer In the nanocomposite and efficient electron transport by MWCNT (significantly higher Incident-photon-to-current conversion efficiency) are suggested to be the possible reasons for the enhancement.

}, keywords = {Carbon nanotubes, charge transfer, Dye-sensitized solar cells, Hybrid composite, hydrothermal}, issn = {1944-8244}, doi = {10.1021/am900396m}, author = {Muduli, Subas and Lee, Wonjoo and Dhas, Vivek V. and Mujawar, Sarfraj and Dubey, Megha and Vijayamohanan, K. and Han, Sung-Hwan and Ogale, Satishchandra} } @article { ISI:000269310700020, title = {Non-templated hydrothermal growth of anisotropic magnetite nanostructures using hexamine as the directing agent}, journal = {Journal of Nanoscience and Nanotechnology}, volume = {9}, number = {10}, year = {2009}, month = {OCT}, pages = {5823-5828}, publisher = {AMER SCIENTIFIC PUBLISHERS}, address = {25650 NORTH LEWIS WAY, STEVENSON RANCH, CA 91381-1439 USA}, abstract = {

Anisotropic growth of magnetite (Fe(3)O(4)) nanoparticles is achieved in a hydrothermal growth process using hexamine to play a dual role of oxide forming and directing agent. The samples are characterized by X-ray diffraction, scanning electron microscopy, high resolution transmission electron microscopy, squid magnetometry, ferromagnetic resonance technique, diffuse reflectance spectroscopy and Mossbauer spectroscopy, which collectively establish the formation of Fe(3)O(4) phase. Anisotropic structures such as nanorods and nanotubules are revealed and these are shown to exhibit good humidity sensing properties.

}, keywords = {Anisotropic Nanostructures, Hexamine, hydrothermal, magnetite, Mossbauer}, issn = {1533-4880}, doi = {10.1166/jnn.2009.1244}, author = {Bhagwat, S. V. and Jouen, Samuel and Kundaliya, D. C. and Singh, H. and Jagadale, Tushar C. and Athawale, A. A. and Lofland, S. E. and Hannoyer, Beatrice and Ogale, Satishchandra B.} } @article { ISI:000291410900022, title = {Controlling stoichiometry in low temperature synthesis of La0.7Sr0.3MnO3 nanoparticles}, journal = {Advanced Science Letters}, volume = {4}, number = {2}, year = {2011}, month = {FEB}, pages = {424-430}, publisher = {AMER SCIENTIFIC PUBLISHERS}, address = {26650 THE OLD RD, STE 208, VALENCIA, CA 91381-0751 USA}, abstract = {

Nanoparticles of complex oxides (\<20 nm) are desirable for several applications in view of the diverse range of physical properties of such oxides. However the simultaneous presence of multiple cation precursors makes the corresponding chemical synthesis non-trivial with possible intermediate evolution of secondary phases. Such phases could react at high temperatures to form the desired stoichiometry, but this process is diffusion limited and can lead to larger particles. In this work we examine the role of three different reaction and growth controlling additives, namely dextran, citric acid and hexamine, on the synthesis of the well known colossal magneto-resistive (CMR) manganite La0.7Sr0.3MnO3. We demonstrate that phase evolutions differ significantly in the three cases, and the physical properties of the products also differ dramatically. Only dextran is shown to yield the desired phase with faceted nanoparticles at as low a temperature as 600 degrees C. A high saturation moment of similar to 47 emu/gm is realized at 10 K with a good square hysteresis loop. In 650 degrees C annealed sample, room temperature magnetization of similar to 15 emu/gm was obtained, which brings the nanoparticles in the applicability domain.

}, keywords = {Citric acid, Complex Oxide, Dextran, Hexamine, hydrothermal}, issn = {1936-6612}, doi = {10.1166/asl.2011.1230}, author = {Azarifar, Ali and Yadav, P. A. and Chawla, A. K. and Jog, Jyoti Prakash and Patil, S. I. and Chandra, Ramesh and Ogale, S. B.} } @article { ISI:000291832600007, title = {Enhanced DSSC performance with high surface area thin anatase TiO2 nanoleaves}, journal = {Solar Energy}, volume = {85}, number = {6, SI}, year = {2011}, month = {JUN}, pages = {1213-1219}, publisher = {PERGAMON-ELSEVIER SCIENCE LTD}, type = {Article}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, ENGLAND}, abstract = {

Thin anatase TiO2 nanoleaves (NLs) with high surface area (similar to 93 m(2)/g) are synthesized by hydrothermal route and dye-sensitized solar cells (DSSC) made using such NLs are compared with those made with hydro-thermally synthesized TiO2 nanoparticles and the Degussa P25 powder. The NLs-based DSSCs show increment of 16\% and 24\% in the total conversion efficiency over the cells made with NPs and P25 respectively. Interestingly, the highest increment in the conversion efficiency (similar to 35\%) is achieved for cells made using a 50:50 (wt/wt) mixture of NLs and NPs. In this case the dye loading is found to be \>50\% higher than the case of NP films. Moreover the DC resistance of diffusion of I-3(-) in electrolyte (as revealed by the electrochemical impedance spectroscopy) is substantially lower than the NP film case, other cell parameters being nominally comparable. (C) 2011 Elsevier Ltd. All rights reserved.

}, keywords = {Dye-sensitized solar cells, Electrochemical impedance spectroscopy, hydrothermal}, issn = {0038-092X}, doi = {10.1016/j.solener.2011.02.029}, author = {Dhas, Vivek V. and Muduli, Subas and Agarkar, Shruti A. and Rana, Abhimanyu and Hannoyer, Beatrice and Banerjee, Rahul and Ogale, Satishchandra B.} } @article { ISI:000294982800015, title = {Surfactant tunable hierarchical nanostructures of CdIn2S4 and their photohydrogen production under solar light}, journal = {International Journal of Hydrogen Energy}, volume = {36}, number = {18}, year = {2011}, month = {SEP}, pages = {11628-11639}, publisher = {PERGAMON-ELSEVIER SCIENCE LTD}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, ENGLAND}, abstract = {

The hierarchical nanostructures of CdIn2S4 were selectively prepared through hydrothermal process in the presence of different surfactants. Structural study demonstrated existence of cubic spinel structure and micro structural study shown a pretty marigold flower like morphology without any surfactant. The effect of surfactants on the morphology and microstructure of CdIn2S4 has been studied by using Polyvinyl pyrrolidone (PVP) and Cetyltrimethyl ammonium bromide (CTAB) as a surfactants. The CdIn2S4 bipyramids with length of 0.7-1 mu m have been obtained using PVP. Interestingly, the nanopetals (thin and transparent) of CdIn2S4 are self assembled into hollow spheres in the presence of CTAB. Considering the importance of these unique nanostructures, the growth mechanism has also been proposed. The optical properties demonstrated the band gap in the range of 2.12-2.29 eV which is well within the visible region. In this contest, photocatalytic activity for hydrogen production using the above nanostructures under visible light was also demonstrated. The prima-fascia observations shows that the bipyramidal CdIn2S4 exhibit excellent photocatalytic activity for hydrogen production (3238 mu molh(-1)) than other nanostructures. Being a nanostructured semiconductor chalcogenide with a good stability will also have potential applications in solar cells and LED. Copyright (C) 2011, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.

}, keywords = {Bipyramids, CdIn2S4, Hydrogen generation, hydrothermal, Self-assembled}, issn = {0360-3199}, doi = {10.1016/j.ijhydene.2011.06.061}, author = {Bhirud, Ashwini P. and Chaudhari, Nilima and Nikam, Latesh and Sonawane, Ravindra and Patil, Kashinath and Baeg, Jin-Ook and Kale, Bharat} } @article { ISI:000289003000012, title = {Synthesis and optical studies of GdCrO3 nanoparticles}, journal = {Journal of Nanoparticle Research}, volume = {13}, number = {3}, year = {2011}, month = {MAR}, pages = {1019-1027}, publisher = {SPRINGER}, address = {VAN GODEWIJCKSTRAAT 30, 3311 GZ DORDRECHT, NETHERLANDS}, abstract = {

{Here we report for the first time, a detailed synthesis mechanism of GdCrO3 nanoparticles using a surfactant-less hydrothermal method. We also report a detailed study of their structural and optical properties. The selected area electron diffraction and powder X-ray diffraction studies of GdCrO3 nanoparticles show pure phase and excellent crystallinity with average particle size around 50-60 nm. The structural analysis indicates a distorted perovskite crystal structure with lattice parameter values of a = 5.3099 +/- A 0.0022

}, keywords = {hydrothermal, Nanoparticles, Rare earth orthochromites}, issn = {1388-0764}, doi = {10.1007/s11051-010-0090-4}, author = {Jaiswal, Adhish and Das, Raja and Adyanthaya, Suguna D. and Poddar, Pankaj} } @article { ISI:000303304900028, title = {TiO2-Au plasmonic nanocomposite for enhanced dye-sensitized solar cell (DSSC) performance}, journal = {Solar Energy}, volume = {86}, number = {5}, year = {2012}, month = {MAY}, pages = {1428-1434}, publisher = {PERGAMON-ELSEVIER SCIENCE LTD}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, ENGLAND}, abstract = {

Anatase TiO2 nanoparticles dressed with gold nanoparticles were synthesized by hydrothermal process by using mixed precursor and controlled conditions. Diffused Reflectance Spectra (DRS) reveal that in addition to the expected TiO2 interband absorption below 360 nm gold surface plasmon feature occurs near 564 nm. It is shown that the dye sensitized solar cells made using TiO2-Au plasmonic nanocomposite yield superior performance with conversion efficiency (CE) of similar to 6\% (no light harvesting), current density (J(SC)) of similar to 13.2 mA/cm(2), open circuit voltage (V-oc) of similar to 0.74 V and fill factor (FF) 0.61; considerably better than that with only TiO2 nanoparticles (CE similar to 5\%, J(SC) similar to 12.6 mA/cm(2), V-oc similar to 0.70 V, FF similar to 0.56). (C) 2012 Elsevier Ltd. All rights reserved.

}, keywords = {Anatase TiO2, Au, Dye-sensitized solar cells, Hybrid composite, hydrothermal}, issn = {0038-092X}, doi = {10.1016/j.solener.2012.02.002}, author = {Muduli, Subas and Game, Onkar S. and Dhas, Vivek V. and Vijayamohanan, K. and Bogle, Kashinath A. and Valanoor, N. and Ogale, Satishchandra B.} } @article { ISI:000344978200061, title = {Hollow Co0.85Se nanowire array on carbon fiber paper for high rate pseudocapacitor}, journal = {ACS Applied Materials \& Interfaces}, volume = {6}, number = {21}, year = {2014}, month = {NOV}, pages = {18844-18852}, publisher = {AMER CHEMICAL SOC}, address = {1155 16TH ST, NW, WASHINGTON, DC 20036 USA}, abstract = {

A supercapacitor electrode is fabricated with Co0.85Se hollow nanowires (HNW) array, which is synthesized by wet chemical hydrothermal selenization of initially grown cobalt hydroxyl carbonate nanowires on conductive CFP. The dense self-organized morphology of Co0.85Se HNWs is revealed by scanning/transmission electron microscopy. The as-synthesized Co0.85Se HNWs possess high pseudocapacitive property with high capacitance retention and high durability. The areal capacitance value is seen to vary from 929.5 to 600 mF cm(-2) (60\% retention) as the current density is increased from 1 to 15 mA cm(-2), an increase of a factor of 15. Based on mass loading, this corresponds to a very high gravimetric capacitance of 674 (for 2 mA cm(-2) or 1.48 Ag-1) and 444 Fg(1-) (for 15 mA cm(-2) or 11 A g(-1)) in a full-cell configuration with the Co0.85Se HNWs as cathode and activated carbon as anode (asymmetric configuration) promising results are obtained.

}, keywords = {asymmetric supercapacitor, carbon fiber paper, cobalt selenide, hydrothermal, pseudocapacitor, selenization}, issn = {1944-8244}, doi = {10.1021/am504333z}, author = {Banerjee, Abhik and Bhatnagar, Sumit and Upadhyay, Kush Kumar and Yadav, Prasad and Ogale, Satishchandra} } @article { ISI:000371105800005, title = {Glucose-derived porous carbon-coated silicon nanowires as efficient electrodes for aqueous micro-supercapacitors}, journal = {ACS Applied Materials \& Interfaces}, volume = {8}, number = {7}, year = {2016}, month = {FEB}, pages = {4298-4302}, publisher = {AMER CHEMICAL SOC}, address = {1155 16TH ST, NW, WASHINGTON, DC 20036 USA}, abstract = {

In this study, we report on carbon coating of vertically aligned silicon nanowire (SiNWs) arrays via a simple hydrothermal process using glucose as carbon precursor. Using this process, a thin carbon layer is uniformly deposited on the SiNWs. Under optimized conditions, the coated SiNWs electrode showed better electrochemical energy storage capacity as well as exceptional stability in aqueous system as compared to uncoated SiNWs. The as-measured capacitance reached 25.64 mF/cm(2) with a good stability up to 25000 charging/discharging cycles in 1 M Na2SO4 aqueous solution.

}, keywords = {carbon coating, glucose precursor, hydrothermal, microsupercapacitors, silicon nanowires}, issn = {1944-8244}, doi = {10.1021/acsami.5b11240}, author = {Devarapalli, Rami Reddy and Szunerits, Sabine and Coffinier, Yannick and Shelke, Manjusha V. and Boukherroub, Rabah} } @article {45714, title = {Enhanced field emission characteristics of a 3D hierarchical Hfo2-Zno heteroarchitecture}, journal = {ChemistrySelect}, volume = {2}, year = {2017}, month = {MAR}, pages = {2305-2310}, type = {Article}, abstract = {

Three dimensional (3D) HfO2-ZnO heteroarchitecture comprised of thin coating of HfO2 on self assembled 3D ZnO urchins with pointed apex has been synthesized using hydrothermal route followed by Pulsed Laser Deposition (PLD). The as-synthesized HfO2-ZnO heteroarchitecture was characterized using XRD, SEM, EDS, and (HR) TEM, in order to reveal its structural, morphological, and chemical properties. The HfO2-ZnO heteroarchitecture emitter exhibits superior field emission (FE) behaviour in contrast to the pristine ZnO urchins, demonstrated by delivery of high emission current density of similar to 885 mA/cm2 at an applied field of similar to 3.35 V/mm, against similar to 383 mA/cm(2) at an applied field of similar to 4.32 V/mu m for the pristine ZnO urchins emitter. Interestingly, the HfO2-ZnO heteroarchitecture emitter exhibits excellent emission current stability characterized with fewer fluctuations, owing to very good ion-bombardment resistance offered by the HfO2 coating. Furthermore, the heteroarchitecture thus obtained facilitates tailoring of the morphology with high aspect ratio and modulation of electronic properties as well, thereby enhancing the FE behaviour. Despite HfO2 being wide band gap and high-k material, the HfO2-ZnO heteroarchitecture exhibits potential as promising candidate for fabrication of high current density cold cathode

}, keywords = {3D heteroarchitecture, Field Emission (FE), hydrothermal, PLD, TEM}, issn = {2365-6549}, doi = {10.1002/slct.201601723}, author = {Shisode, Raju T. and Suryawanshi, Sachin R. and Mistari, Chetan D. and Late, Dattatray J. and More, Mahendra A.} } @article {46751, title = {Nonenzymatic glucose detection in human serum using Ni nanoparticles decorated reduced graphene oxide}, journal = {Science of Advanced Materials}, volume = {12}, year = {2020}, month = {AUG}, pages = {1125-1136}, type = {Article}, abstract = {

Reduced Graphene oxide (RGO) decorated with Ni nanoparticles (NiNPs) composites, have been successfully synthesized using a simple hydrothermal method and possessing excellent electrocatalytic activity towards glucose oxidation. The morphological and structural features of RGO-Ni nanocomposites were characterized by field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS) and energy dispersive spectroscopy (EDS). From TEM, we observed that NiNPs were anchored on RGO sheets. Cyclic Voltammetric (CV) study revealed that the electrocatalytic activity of RGO-Ni nanocomposite with 20\% Ni loading (RGONi-20) towards glucose oxidation is better than that shown by bare Glassy Carbon Electrode (GCE), RGO, bare NiNPs, RGONi10 and RGONi-30. The prepared nanocomposites exhibited fast electrocatalytic response (\<5 s) towards glucose oxidation. Amperometric study indicates that the present glucose sensor have exhibited excellent performance by offering a lowest detection limit as 5.1 mu M, with linier range from 2 to 5000 mu M and high sensitivity of 896.67 mu A mM(-1) cm(-2). Interference from different anticipatable electroactive substances such as ascorbic acid (AA), uric acid (UA) and dopamine (DA) is not observed. Furthermore, the application of the as prepared sensor was successfully demonstrated for the detection of glucose in human serum and results were comparable to presently used nonenzymatic technique. RGONi-20 nanocomposite electrode holds great promise for the development of biosensors and other electrochemical devices.

}, keywords = {Electrochemical, Glucose Sensor, Graphene-Nickel Nanoparticles, hydrothermal, Nanocomposite, Nonenzymatic}, issn = {1947-2935}, doi = {10.1166/sam.2020.3776}, author = {Waichal, Rupali and Bhirud, Ashwini and Fouad, H. and Gosavi, Suresh and Ashokkumar, Muthupandian} } @article {47456, title = {Zinc-air batteries catalyzed using Co3O4 nanorod-supported N-doped entangled graphene for oxygen reduction reaction}, journal = {ACS Applied Energy Materials}, volume = {4}, year = {2021}, month = {MAY }, pages = {4570-4580}, type = {Article}, abstract = {

The work reported here deals with the development of an efficient non-platinum electrocatalyst for electrochemical oxygen reduction reaction (ORR) through a sequential pathway involving hydrothermal treatment followed by freeze-drying to build the desired structural architecture of the catalyst. The designed catalyst (Co3O4/nitrogen-doped entangled porous 3D graphene (NEGF)), which contains Co3O4 nanorods anchored on the surface of three-dimensional (3D)-structured N-doped graphene, was found to display higher ORR activity during single-electrode testing and demonstrate a Zn-air battery (ZAB) system. Under the hydrothermal treatment at 180 degrees C, in the presence of ammonia, nitrogen was doped into the carbon framework of graphene, which subsequently formed a self-assembled entangled 3D structure of graphene after freeze-drying. The hydrothermal treatment and freeze-drying processes were found to play vital roles in tuning the morphological and structural features of the catalyst. The doped nitrogen, apart from its favorable contribution toward ORR, helped facilitate efficient dispersion of oxide nanorods on graphene. Co3O4/NEGF displayed remarkable ORR activity in 0.1 M KOH solution, as evident from the 60 mV onset potential shift compared to the state-of-the-art Pt/C catalyst and the Tafel slope value of 74 mV dec(-1) vs 68 mV dec(-1) for Pt/C. The ZAB fabricated by employing Co3O4/NEGF as the cathode catalyst was found to be an efficient competitor for the system based on the Pt/C cathode. This high performance has been credited to the controlled interplay of the governing factors such as the interfacial interactions leading to the efficient dispersion of metal oxide nanorods, increased catalyst surface area, the cooperative effect arising from the defects present in the N-doped porous 3D graphene, and the synergetic interactions operating in the system.

}, keywords = {cobalt-oxide nanorod, freeze-drying, hydrothermal, N-doped entangled graphene, oxygen reduction reaction, zinc-air battery}, issn = {2574-0962}, doi = {10.1021/acsaem.1c00210}, author = {Manna, Narugopal and Singh, Santosh K. and Kharabe, Geeta Pandurang and Torris, Arun and Kurungot, Sreekumar} } @article {48134, title = {Sponge microflowers of NiCo2O4: a versatile material for high performance supercapacitor}, journal = {Journal of Porous Materials}, volume = {29}, year = {2022}, month = {AUG}, pages = {1239-1252}, type = {Article}, abstract = {

We report the development of well optimised NiCo2O4 microflowers for high performance supercapacitor application. The efforts were made to optimise the electrode material by tuning the synthetic as well as electrolyte concentration parameters such as (i) hydrothermal reaction temperature, (ii) hydrothermal reaction time, (iii) sintering temperature, and (iv) electrolyte concentration. The physico-chemical and supercapacitive properties were analysed using TGA, XRD, SEM/TEM/HRTEM, XPS, BET, and electrochemical measurements. The well optimised electrode material was obtained at 150 degrees C hydrothermal reaction temperature, 12 h of hydrothermal reaction time, 300 degrees C sintering temperature, and 3 M KOH electrolyte concentration. The optimised sample displayed high specific -capacitance (1478 F/g), -energy density (16.5 Wh/kg), and -power density (248 W/kg). The specific capacitance can be retained to 97.61\% after 1000 cycles. The developed NiCo2O4 microflower structures are well optimised and offer great promise for future industrial applications.

}, keywords = {hydrothermal, Microflowers, Nickel cobaltite, supercapacitor}, issn = {1380-2224}, doi = {10.1007/s10934-022-01247-9}, author = {Ghadage, Ambar and Kodam, Pavan and Nadargi, Digambar and Shinde, K. P. and Mulla, Imtiaz and Park, J. S. and Suryavanshi, Sharad} }