01965nas a2200217   4500008004100000022001400041245014600055210006900201260009900270300001000369490000700379520107700386653001901463653001401482653002801496100002601524700002101550700002801571700002201599856012601621       2016                        eng d  a0032-386100aIncorporation of rigid polyaromatic groups in polybenzimidazole-based polymeric ionic liquids: assertive effects on gas permeation properties0 aIncorporation of rigid polyaromatic groups in polybenzimidazoleb  aTHE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLANDbELSEVIER SCI LTDcJUN  a30-360 v933 a<p>Polymeric ionic liquids (PILs) have emerged as promising membrane materials for CO2 separation. The present work is aimed at investigating the effects of incorporation of rigid polyaromatic hydrocarbons, viz., pyrene and anthracene, in polybenzimidazole-based PILs. The effects of substituent and anion variation on the gas permeation properties of PILs using pure gases were examined at 20 atm upstream pressure. The results were correlated with physical properties of PILs. The pyrene substituted PIL exhibited similar to 10 fold increase in CO2 permeability as compared to its precursor polymer PBI-BuI. The combination of a CO2 specific anion and bulky group substitution offered higher CO2 permeability as well as appreciable permselectivity than their structural analogue that was devoid of IL functionality. The permeation properties of present PILs were superior to those of conventional glassy polymers such as polysulfone, matrimid and polycarbonate which are widely studied for their gas permeation properties. (C) 2016 Elsevier Ltd. All rights reserved.</p>10aGas permeation10amembranes10aPolymeric ionic liquids1 aShaligram, Sayali, V.1 aRewar, Anita, S.1 aWadgaonkar, Prakash, P.1 aKharul, Ulhas, K.  uhttp://library.ncl.res.in/content/incorporation-rigid-polyaromatic-groups-polybenzimidazole-based-polymeric-ionic-liquids02570nas a2200241   4500008004100000022001400041245012400055210006900179260000900248300001000257490000700267520172200274653001501996653001902011653002802030653001402058653003302072100002102105700002602126700002202152700002802174856012602202       2018                        eng d  a0887-624X00aSynthesis, characterization, and gas permeation properties of adamantane-containing polymers of intrinsic microporosity0 aSynthesis characterization and gas permeation properties of adam  cJAN   a16-240 v563 a<p>A new bis(catechol) monomer, namely, 4,4-((1r,3r)-adamantane-2,2-diyl)bis(benzene-1,2diol) (THADM) was synthesized by condensation of 2-adamantanone with veratrole followed by demethylation of the formed (1r,3r)-2,2-bis(3,4 dimethoxyphenyl)adamantane. Polycondensation of THADM and various compositions of THADM and 5,5,6,6-tetrahydroxy-3,3,3,3-tetramethylspirobisindane was performed with 2,3,5,6-tetrafluoroterephthalonitrile (TFTPN) to obtain the homopolymer and copolymers. These polymers demonstrated good solubility in common organic solvents such as dichloromethane, chloroform, and tetrahydrofuran and could be cast into tough films from their chloroform solutions. GPC analysis revealed that number average molecular weights of polymers were in the range 48,100-61,700 gmol(-1), suggesting the formation of reasonably high molecular weight polymers. They possessed intrinsic microporosity with Brunauer-Emmett-Teller (BET) surface area in the range 703-741 m(2)g(-1). Thermogravimetric analysis of polymers indicated that 10% weight loss temperature was in the range 513-518 degrees C demonstrating their excellent thermal stability. THADM-based polymer of intrinsic microporosity (PIM) showed P(CO2)=1080, P(O-2)=232 and appreciable selectivity [(CO2/CH4)=22.6, (CO2/N-2)=26.7, and (O-2/N-2)= 5.7]. The gas permeability measurements revealed that with increase in the content of adamantane units in PIMs, selectivity increased and permeability decreased, following the trade-off relationship. The gas separation properties of PIMs containing adamantane units were located close to 2008 Robeson upper bound for gas pairs such as CO2/CH4, CO2/N-2, H-2/N-2, and O-2/N-2. (c) 2017 Wiley Periodicals, Inc.</p>10aadamantane10aGas permeation10aintrinsic microporosity10amembranes10astructure-property relations1 aShrimant, Bharat1 aShaligram, Sayali, V.1 aKharul, Ulhas, K.1 aWadgaonkar, Prakash, P.  uhttp://library.ncl.res.in/content/synthesis-characterization-and-gas-permeation-properties-adamantane-containing-polymers