02909nas a2200265   4500008004100000022001400041245014100055210006900196260000900265300001400274490000700288520197300295653001902268653002102287653002302308653002802331653002102359100002702380700002402407700002702431700002102458700001802479700002402497856012202521       2020                        eng d  a0947-653900aHierarchical nanoflower arrays of Co9S8-Ni3S2 on nickel foam: a highly efficient binder-free electrocatalyst for overall water splitting0 aHierarchical nanoflower arrays of Co9S8Ni3S2 on nickel foam a hi  cJUN   a7900-79110 v263 a<p>Hydrogen production is vital for meeting future energy demands and managing environmental sustainability. Electrolysis of water is considered as the suitable method for H-2 generation in a carbon-free pathway. Herein, the synthesis of highly efficient Co9S8-Ni3S2 based hierarchical nanoflower arrays on nickel foam (NF) is explored through the one-pot hydrothermal method (Co9S8-Ni3S2/NF) for overall water splitting applications. The nanoflower arrays are self-supported on the NF without any binder, possessing the required porosity and structural characteristics. The obtained Co9S8-Ni3S2/NF displays high hydrogen evolution reaction (HER), as well as oxygen evolution reaction (OER), activities in 1 m KOH solution. The overpotentials exhibited by this system at 25 mA cm(-2) are nearly 277 and 102 mV for HER and OER, respectively, in 1 m KOH solution. Subsequently, the overall water splitting was performed in 1 m KOH solution by employing Co9S8-Ni3S2/NF as both the anode and cathode, where the system required only 1.49, 1.60, and 1.69 V to deliver the current densities of 10, 25, and 50 mA cm(-2), respectively. Comparison of the activity of Co9S8-Ni3S2/NF with the state-of-the-art Pt/C and RuO2 coated on NF displays an enhanced performance for Co9S8-Ni3S2/NF both in the half-cell as well as in the full cell, emphasizing the significance of the present work. The post analysis of the material after water electrolysis confirms that the surface Co(OH)(2) formed during the course of the reaction serves as the favorable active sites. Overall, the activity modulation achieved in the present case is attributed to the presence of the open-pore morphology of the as formed nanoflowers of Co9S8-Ni3S2 on NF and the simultaneous presence of the surface Co(OH)(2) along with the highly conducting Co9S8-Ni3S2 core, which facilitates the adsorption of the reactants and subsequently its conversion into the gaseous products during water electrolysis.</p>
10acobalt sulfide10aelectrocatalysts10aHydrogen evolution10aoverall water splitting10aoxygen evolution1 aIllathvalappil, Rajith1 aWalko, Priyanka, S.1 aKanheerampockil, Fayis1 aBhat, Suresh, K.1 aDevi, Nandini1 aKurungot, Sreekumar  uhttp://library.ncl.res.in/content/hierarchical-nanoflower-arrays-co9s8-ni3s2-nickel-foam-highly-efficient-binder-free02612nas a2200265   4500008004100000022001400041245009000055210006900145260000800214300001200222490000800234520176400242653003602006653000802042653001402050653002802064653000802092653002802100100001802128700001902146700001802165700002202183700002402205856011702229       2025                        eng d  a0360-319900aGrowth of Mo-doped Ni3S2 nanorods array for superior overall water splitting reaction0 aGrowth of Modoped Ni3S2 nanorods array for superior overall wate  cJUN  a729-7370 v1413 a<p>
	Designing novel, efficient and cost-effective dual-functional electrocatalyst for hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) using an alkaline electrolyte is crucial for establishing a sustainable hydrogen economy and transitioning to a society powered by renewable energy sources. In the present work, Mo-doped nickel sulfide (Mo-Ni3S2) nanorods were grown on Ni-treated nickel foam (N-NF) substrate via a two-steps hydrothermal method. Specifically, Mo-Ni3S2/N-NF surface consists of nanorods-like morphology, which provides extensive area for percolation of electrolyte, that resulting in outstanding catalytic performance. Such a well-synthesized electrode exhibited superior performance and stability for OER as compared with pristine Ni3S2/NF and bare nickel foam (NF) electrodes. In addition, Mo-Ni3S2/N-NF electrode provides good HER activity and confirms its dual-functionality in alkaline medium. Our champion Mo-Ni3S2/N-NF electrocatalyst delivers best OER overpotential of 230 mV at current density of 100 mA/cm(2). Also, it provides HER overpotential of 100.6 mV at a current density of 10 mA/cm(2). Both OER and HER are carried out in the presence of 1 M KOH alkaline electrolyte. OER stability of the best-performed Mo-Ni3S2/N-NF electrode demonstrates almost constant current density similar to 120 mA/cm(2), which retains 90% of original value after continuously tested for the duration of 22 h. The total cell voltage of 1.56 V is provided by Mo-Ni3S2/N-NF integrated system and it demonstrates a good stability for duration of 22 h. Our approach provides a new insight into developing earth-abundant, inexpensive and superior dual-functional electrocatalyst for overall water splitting reaction (WSR).</p>
10aDual-functional electrocatalyst10aHER10aMo doping10aNickel sulfide nanorods10aOER10aoverall water splitting1 aSharma, Pooja1 aKhandare, Lina1 aSaha, Arindam1 aChaure, Nandu, B.1 aYengantiwar, Ashish  uhttp://library.ncl.res.in/content/growth-mo-doped-ni3s2-nanorods-array-superior-overall-water-splitting-reaction